| 布氏硬度 HB | 洛氏硬度 | 维氏 硬度 HV | 布氏硬度 HB | 洛氏硬度 | 维氏硬度 HV | ||
| HRA | HRC | HRA | HRC | ||||
| 86,6 | 70,0 | 1037 | 78,5 | 55,0 | 599 | ||
| 86,3 | 69,5 | 1017 | 78,2 | 54,5 | 589 | ||
| 86,1 | 69,0 | 997 | 77,9 | 54,0 | 579 | ||
| 85,8 | 68,5 | 978 | 77,7 | 53,5 | 570 | ||
| 85,5 | 68,0 | 959 | 77,4 | 53,0 | 561 | ||
| 85,2 | 67,5 | 941 | 77,1 | 52,5 | 551 | ||
| 85,0 | 67,0 | 923 | 76,9 | 52,0 | 543 | ||
| 84,7 | 66,5 | 906 | 76,6 | 51,5 | 534 | ||
| 84,4 | 66,0 | 889 | 501 | 76,3 | 51,0 | 525 | |
| 84,1 | 65,5 | 872 | 494 | 76,1 | 50,5 | 517 | |
| 83,9 | 65,0 | 856 | 488 | 75,8 | 50,0 | 509 | |
| 83,6 | 64,5 | 840 | 481 | 75,5 | 49,5 | 501 | |
| 83,3 | 64,0 | 825 | 474 | 75,3 | 49,0 | 493 | |
| 83,1 | 63,5 | 810 | 468 | 75,0 | 48,5 | 485 | |
| 82,8 | 63,0 | 795 | 461 | 74,7 | 48,0 | 478 | |
| 82,5 | 62,5 | 780 | 455 | 74,5 | 47,5 | 470 | |
| 82,2 | 62,0 | 766 | 449 | 74,2 | 47,0 | 463 | |
| 82,0 | 61,5 | 752 | 442 | 73,9 | 46,5 | 456 | |
| 81,7 | 61,0 | 739 | 436 | 73,7 | 46,0 | 449 | |
| 81,4 | 60,5 | 726 | 430 | 73,4 | 45,5 | 443 | |
| 81,2 | 60,0 | 713 | 424 | 73,2 | 45,0 | 436 | |
| 80,9 | 59,5 | 700 | 418 | 72,9 | 44,5 | 429 | |
| 80,6 | 59,0 | 688 | 413 | 72,6 | 44,0 | 423 | |
| 80,3 | 58,5 | 676 | 407 | 72,4 | 43,5 | 417 | |
| 80,1 | 58,0 | 664 | 401 | 72,1 | 43,0 | 411 | |
| 79,8 | 57,5 | 653 | 396 | 71,8 | 42,5 | 405 | |
| 79,5 | 57,0 | 642 | 391 | 71,6 | 42,0 | 399 | |
| 79,3 | 56,5 | 631 | 385 | 71,3 | 41,5 | 393 | |
| 79,0 | 56,0 | 620 | 380 | 71,1 | 41,0 | 388 | |
| 78,7 | 55,5 | 609 | 375 | 70,8 | 40,5 | 382 | |
Jernholdige metalmaterialer hårdhedsværdi konverteringstabel
| 布氏硬度 HB | 洛氏硬度 | 维氏硬度 HV | 布氏硬度 HB | 洛氏硬度 | 维氏硬度 HV | ||
| HRA | HRC | HRA | HRC | ||||
| 370 | 70,5 | 40,0 | 377 | 269 | 28,0 | 274 | |
| 365 | 70,3 | 39,5 | 372 | 266 | 27,5 | 271 | |
| 360 | 70,0 | 39,0 | 367 | 263 | 27,0 | 268 | |
| 355 | 38,5 | 362 | 260 | 26,5 | 264 | ||
| 350 | 38,0 | 351 | 257 | 26,0 | 261 | ||
| 345 | 37,5 | 352 | 254 | 25,5 | 258 | ||
| 341 | 37,0 | 347 | 251 | 25,0 | 255 | ||
| 336 | 36,5 | 342 | 248 | 24.5 | 252 | ||
| 332 | 36,0 | 338 | 245 | 24,0 | 249 | ||
| 327 | 35,5 | 333 | 242 | 23.5 | 246 | ||
| 323 | 35,0 | 329 | 240 | 23,0 | 243 | ||
| 318 | 34,5 | 324 | 237 | 22.5 | 240 | ||
| 314 | 34,0 | 320 | 234 | 22,0 | 237 | ||
| 310 | 33,5 | 316 | 232 | 21.5 | 234 | ||
| 306 | 33,0 | 312 | 229 | 21.0 | 231 | ||
| 302 | 32,5 | 308 | 227 | 20.5 | 229 | ||
| 298 | 32,0 | 304 | 225 | 20.0 | 226 | ||
| 294 | 31,5 | 300 | 222 | 19.5 | 223 | ||
| 291 | 31,0 | 296 | 220 | 19,0 | 221 | ||
| 287 | 30,5 | 292 | 218 | 18.5 | 218 | ||
| 283 | 30,0 | 289 | 216 | 18,0 | 216 | ||
| 280 | 29,5 | 285 | 214 | 17.5 | 214 | ||
| 276 | 29,0 | 281 | 211 | 17,0 | 211 | ||
| 273 | 28,5 | 278 | |||||
Note:
1. Brinell hårdhed: Det bruges hovedsageligt til at måle hårdheden af støbegods, smedegods, ikke-jernholdige metaldele, varmvalsede barrer og udglødede dele. Måleområdet er ≥HB450.
2. Rockwell hårdhed: HRA bruges hovedsageligt til prøver med høj hårdhed til at måle overfladehårdheden af materialer og overflader med hårdhed højere end HRC67, såsom hårdmetal, nitreret stål osv. Måleområdet er HRA>70. HRC bruges hovedsageligt til at måle hårdheden af ståldele (såsom kulstofstål, værktøjsstål, legeret stål osv.) efter bratkøling eller anløbning. Måleområdet er HRC20~67.
3. Vickers hårdhed: bruges til at måle hårdheden af tynde dele og stålpladedele, og kan også bruges til at måle hårdheden af overfladehærdede dele såsom karburering, cyanering og nitrering.